Materials

>

Fibers

FIBERS

Carbon Fiber

MARKFORGED

High stiffness, high tensile strength, and low weight

Carbon Fiber

Technical Datasheet
Process: CFR 3D Printing
Tensile Strength at Yield

800 MPa | 116 ksi

Tensile Modulus

60 GPa | 8702 ksi

Elongation at Break

1.5%

Impact Strength (Notched)

960 J/m | 18 ft-lb/in

Heat Deflection Temperature

105 °C | 221 °F

Kevlar

MARKFORGED

High strength, resistant to fatigue, and low weight

Kevlar

Technical Datasheet
Process: CFR 3D Printing
Tensile Strength at Yield

610 MPa | 88 ksi

Tensile Modulus

27 GPa | 3916 ksi

Elongation at Break

2.7%

Impact Strength (Notched)

2000 J/m | 37.5 ft-lb/in

Heat Deflection Temperature

105 °C | 221 °F

Fiberglass

MARKFORGED

High strength, high impact strength, and low weight

Fiberglass

Technical Datasheet
Process: CFR 3D Printing
Tensile Strength at Yield

590 MPa | 86 ksi

Tensile Modulus

21 GPa | 3046 ksi

Elongation at Break

3.8%

Impact Strength (Notched)

2600 J/m | 48.7 ft-lb/in

Heat Deflection Temperature

105 °C | 221 °F

HSHT Fiberglass

MARKFORGED

High impact strength, high HDT, and low weight

High strength high temperature fiberglass

Technical Datasheet
Process: CFR 3D Printing
Tensile Strength at Yield

600 MPa | 87 ksi

Tensile Modulus

21 GPa | 3046 ksi

Elongation at Break

3.9%

Impact Strength (Notched)

3100 J/m | 58.1 ft-lb/in

Heat Deflection Temperature

150 °C | 302 °F