MARKFORGED
Fiberglass
590 MPa
86 ksi
Tensile Strength at Yield
2600 J/m
48.7 ft-lb/in
Impact Strength (Notched)
21 GPa
3046 ksi
Tensile Modulus
590 MPa
86 ksi
Tensile Strength at Yield
2600 J/m
48.7 ft-lb/in
Impact Strength (Notched)
21 GPa
3046 ksi
Tensile Modulus
Characteristics
Description:
Fiberglass is a material capable of making parts 10x stronger than ABS when laid with a composite base. Fiberglass is a more affordable alternative to Carbon Fiber, perfect for hand tools insulation, and medium strength equipment.
Cost:
$$$
$$
Typical Lead Time:
1-2 Days
Layer Height:
Standard 0.1 mm
Manufacturing Processes:
Continuous Fiber Reinforcement
Material Properties
Tensile Strength:
590 MPa
Tensile Modulus:
21 GPa
Tensile Strain at Break:
3.8 %
Flexural Strength:
200 MPa
Flexural Modulus:
22 GPa
Flexural Strain at Break:
1.1 %
Compressive Strength:
140 MPa
Compressive Modulus:
21 MPa
Heat Deflection Temp:
105 °C
Izod Impact (notched):
2600 J/m
Density:
1.5 g/cm3