HSHT Fiberglass

600 MPa

87 ksi

Tensile Strength at Yield

3100 J/m

58.1 ft-lb/in

Impact Strength (Notched)

150 °C

302 °F

Heat Deflection Temperature

600 MPa

87 ksi

Tensile Strength at Yield

3100 J/m

58.1 ft-lb/in

Impact Strength (Notched)

150 °C

302 °F

Heat Deflection Temperature

Characteristics

Description:

High Strength High Temperature (HSHT) Fiberglass is high in strength and keeps its strength in high and low temperatures. This allows parts with HSHT reinforcement to keep their strength in high-temperature environments like mold and cleaning processes.

Cost:

$$$

$$

Typical Lead Time:

1-2 Days

Layer Height:

Standard 0.1 mm

Manufacturing Processes:

Continuous Fiber Reinforcement

Get a Quote for HSHT Fiberglass

Material Properties

Tensile Strength:

600 MPa

Tensile Modulus:

21 GPa

Tensile Strain at Break:

3.9 %

Flexural Strength:

420 MPa

Flexural Modulus:

21 GPa

Flexural Strain at Break:

2.2 %

Compressive Strength:

192 MPa

Compressive Modulus:

21 MPa

Heat Deflection Temp:

150 °C

Izod Impact (notched):

3100 J/m

Density:

1.5 g/cm3