Material Type

Metal

Material Sub-Type

Stainless Steel

Material Name

Stainless Steel 17-4 PH

Stainless steel 17-4 PH is a type of martensitic precipitation-hardening stainless steel. It is composed of about 17% chromium, 4% nickel, and 4% copper. This combination of elements gives the material excellent corrosion resistance, as well as high strength and hardness. It is commonly used in applications that require high strength and corrosion resistance, such as aerospace and defense components, and oil and gas industry parts. It can be heat treated to achieve a range of mechanical properties, making it a versatile material.

Cost
Lead Time

2-3 Days

Processes

CNC Machining

Metric

English

Note: Properties are not guaranteed. They are intended only as a basis for comparison and not for design purposes.

Last Updated:6 days ago
Mechanical Properties

Yield Tensile Strength

1000 MPa

Ultimate Tensile Strength

1103 MPa

Tensile Modulus

193 GPa

Shear Strength

827 MPa

Shear Modulus

76 GPa

Fatigue Strength

676 MPa

Elongation At Break

15 %

Poisson's Ratio

0.28

Hardness

C36/365

Density

7.8 g/cm³

Impact Strength (ASTM)

-

Electrical/Magnetic Properties

Surface Resistance (ANSI)

83.0 µΩ

Magnetism

High

Thermal Properties

Heat Deflection Temperature

-

Thermal Expansion Coefficient

11.0 µm/(m⋅°C

Specific Heat Capacity

0.460 J/g°C

Thermal Conductivity

16.4 W/(m⋅°C)

Melting Point

1400 °C

Chemical Properties

Corrosion Resistance

Excellent

Stainless Steel 17-4 PH

Tough and hardenable stainless steel

Get your parts manufactured today.

Get Instant Quote

Material Datasheet

Material Type

Metal

Material Sub-Type

Stainless Steel

Material Name

Stainless Steel 17-4 PH

Note: Properties are not guaranteed. They are intended only as a basis for comparison and not for design purposes.

Mechanical Properties

Yield Tensile Strength

1000 MPa

145.0 Ksi

Ultimate Tensile Strength

1103 MPa

160.0 Ksi

Tensile Modulus

193 GPa

28.0 Msi

Shear Strength

827 MPa

120.0 Ksi

Shear Modulus

76 GPa

11.0 Msi

Fatigue Strength

676 MPa

98.0 Ksi

Elongation At Break

15 %

-

Poisson's Ratio

0.28

-

Hardness

C36/365

-

Density

7.8 g/cm³

0.282 lb/in³

Impact Strength (ASTM)

-

-

Electrical/Magnetic Properties

Surface Resistance (ANSI)

83.0 µΩ

-

Magnetism

High

-

Thermal Properties

Heat Deflection Temperature

-

-

Thermal Expansion Coefficient

11.0 µm/(m⋅°C

6.1 µin/(in⋅°F)

Specific Heat Capacity

0.460 J/g°C

0.110 BTU/lb-°F

Thermal Conductivity

16.4 W/(m⋅°C)

9.5 BTU/(h⋅ft⋅°F)

Melting Point

1400 °C

2552 °F

Chemical Properties

Corrosion Resistance

Excellent

-

www.protoxyz.com