Aluminum 6061-T6_T651_T6511 is a heat-treated structural aluminum alloy that is commonly used in the aerospace, transportation, and construction industries. It has a high strength-to-weight ratio, making it an ideal material for applications where weight is a critical factor. It is also highly resistant to corrosion, making it well-suited for use in marine environments. In addition, the alloy has good machinability and is easily weldable, making it a versatile option for many manufacturing processes. It is also relatively easy to form and has excellent surface finish capabilities, making it an attractive choice for many applications.
Cost
Lead Time
2-3 Days
Processes
CNC Machining
Metric
English
Note: Properties are not guaranteed. They are intended only as a basis for comparison and not for design purposes.
Mechanical Properties
Yield Tensile Strength
276 MPa
Ultimate Tensile Strength
310 MPa
Tensile Modulus
69 GPa
Shear Strength
207 MPa
Shear Modulus
26 GPa
Fatigue Strength
97 MPa
Elongation At Break
17 %
Poisson's Ratio
0.33
Hardness
B60/95
Density
2.7 g/cm³
Impact Strength (ASTM)
-
Electrical/Magnetic Properties
Surface Resistance (ANSI)
4.0 µΩ
Magnetism
Non-Magnetic
Thermal Properties
Heat Deflection Temperature
130 °C
Thermal Expansion Coefficient
23.6 µm/(m⋅°C
Specific Heat Capacity
0.896 J/g°C
Thermal Conductivity
167 W/(m⋅°C)
Melting Point
582 °C
Chemical Properties
Corrosion Resistance
Very Good